CYCOLOY PC/ABS C4215HF物性表

Cycoloy C4215HF is a 15% glass reinforced, non-FR PC+ABS grade with high heat resistance, excellent strength and rigidity with good cosmetic apprearance. It combines good processability with a low shrinkage.

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min
95
MPa
ISO 527
Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min
3
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
5550
MPa
ISO 527
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
4700
MPa
ISO 178
IMPACT
Value Unit Standard
Izod IMPACT, unnotched 80*10*3 +23°C
0
kJ/m2
ISO 180/1U
Izod IMPACT, unnotched 80*10*3 -30°C
0
kJ/m2
ISO 180/1U
Izod IMPACT, notched 80*10*3 +23°C / 悬壁梁缺口冲击强度, 80*10*3 +23°C
0
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*3 -30°C / 悬壁梁缺口冲击强度, 80*10*3 -30°C
0
kJ/m2
ISO 180/1A
Izod IMPACT, unnotched 80*10*4 +23°C
33
kJ/m2
ISO 180/1U
Izod IMPACT, unnotched 80*10*4 -30°C
37
kJ/m2
ISO 180/1U
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
8
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
7
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*3 sp=62mm
9
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,-30°C,C80*10*3 sp=62mm
7
kJ/m2
ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
38
kJ/m2
ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
44
kJ/m2
ISO 179/1eU
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
136
°C
ISO 306
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
137
°C
ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距
129
°C
ISO 75/Af
PHYSICAL
Value Unit Standard
Density/密度
1.25
g/cm3
ISO 1183
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
0.6
%
ISO 62
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
0.2
%
ISO 62
Melt Volume Rate, MVR at 260°C/5.0 kg / 溶化体积流率,MVR, 260°C/5.0 kg
31
cm3/10 min
ISO 1133
Source GMD, last updated:03/20/2008
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
100 – 110
°C
Drying Time / 干燥时间
2 – 4
hrs
Melt Temperature / 熔体温度
240 – 280
°C
Mold Temperature / 模具温度
50 – 80
°C